Capacitors

ABSTRACT

Back end of the line (BEOL) capacitors and methods of manufacture are provided. The method includes forming wiring lines on a substrate, with spacing between adjacent wiring lines. The method further includes forming an air gap within spacing between the adjacent wiring lines by deposition of a capping material. The method further includes opening the air gap between selected adjacent wiring lines. The method further includes depositing conductive material within the opened air gap.

FIELD OF THE INVENTION

The invention relates to semiconductor structures and, moreparticularly, to back end of the line (BEOL) capacitors and methods ofmanufacture.

BACKGROUND

Vertical natural capacitors are on-chip capacitors that are incorporatedinto the interconnect levels of integrated circuits, typically duringback end of line (BEOL) processes. Such capacitors are currently used ascapacitor devices in many logic and analog semiconductor technologies.These capacitors may be placed in close proximity to various componentson the integrated circuit in order to minimize inductive or resistivelosses that may occur when using off-chip capacitors. As technologyscaling continues, the capacitance density for such capacitors isexpected to increase; however, the circuit density increases, thecapacitance tends to drop.

SUMMARY

In an aspect of the invention, a method comprises forming wiring lineson a substrate, with spacing between adjacent wiring lines. The methodfurther comprises forming an air gap within spacing between the adjacentwiring lines by deposition of a capping material. The method furthercomprises opening the air gap between selected adjacent wiring lines.The method further comprises depositing conductive material within theopened air gap.

In an aspect of the invention, a method comprises forming wiring lineson a substrate, with spacing between adjacent wiring lines. The methodfurther comprises forming an air gap within the spacing by depositingcapping material on the wiring lines and within the spacing between theadjacent wiring until the capping material becomes pinched off. Themethod further comprises forming a dielectric material over the cappingmaterial including over the air gaps. The method further comprisesforming a trench in the dielectric material over the air gaps. Themethod further comprises removing a bottom surface of the trench andunderlying capping material to open the air gaps. The method furthercomprises depositing conductive material within the trench and withinthe opened air gaps.

In an aspect of the invention, a back end of line capacitor comprises: abottom plate comprising a plurality of metal lines separated by spacing;a dielectric layer lining the metal lines within the spacing; and a topplate above the metal lines and within the spacing over the dielectricmaterial.

BRIEF DESCRIPTION OF THE DRAWINGS

The present invention is described in the detailed description whichfollows, in reference to the noted plurality of drawings by way ofnon-limiting examples of exemplary embodiments of the present invention.

FIG. 1 shows a starting structure and respective fabrication processesin accordance with aspects of the invention.

FIG. 2 shows formation of air gaps between metal lines and respectivefabrication processes in accordance with aspects of the invention.

FIG. 3 shows offset trenches and respective fabrication processes inaccordance with aspects of the invention.

FIG. 4 shows an opening to the air gap from a trench and respectivefabrication processes in accordance with aspects of the invention.

FIG. 5 shows a metal fill within the air gap and the plurality oftrenches and respective fabrication processes in accordance with aspectsof the invention.

DETAILED DESCRIPTION

The invention relates to semiconductor structures and, moreparticularly, to back end of the line (BEOL) capacitors and methods ofmanufacture. More specifically, the present invention is directed to aBEOL plate capacitor and methods of manufacturing using copper etch backand air gap processes. In embodiments, the capacitor can also be a combpattern of wider or narrower lines. Moreover, the capacitor can land ona prior airgap level, and the lines could be perpendicular to the gapsbelow. Advantageously, the BEOL capacitor described herein allows fordevice scaling accompanied by increased capacitance density. In furtherembodiments, the BEOL capacitor can be used with ultra low dielectricconstantmaterials while still allowing for device scaling andaccompanied by increased capacitance density (over conventionalstructures). In embodiments, the BEOL capacitor is a vertical naturalcapacitor.

The capacitor of the present invention can be manufactured in a numberof ways using a number of different tools. In general, though, themethodologies and tools are used to form structures with dimensions inthe micrometer and nanometer scale. The methodologies, i.e.,technologies, employed to manufacture the plate capacitor of the presentinvention have been adopted from integrated circuit (IC) technology. Forexample, the structures of the present invention are built on wafers andare realized in films of material patterned by photolithographicprocesses on the top of a wafer. In particular, the fabrication of theplate capacitor of the present invention uses three basic buildingblocks: (i) deposition of thin films of material on a substrate, (ii)applying a patterned mask on top of the films by photolithographicimaging, and (iii) etching the films selectively to the mask.

FIG. 1 shows a starting structure and respective fabrication processesin accordance with aspects of the invention. The starting structure 10is a BEOL structure which includes an etch stop layer 12. The etch stoplayer 12 protects lower wiring and device layers from BEOL processes, aswell as acting as a barrier diffusion layer for copper or other metals.In embodiments, the etch stop layer 12 can be a nitride layer, SiN orSiNC (NBLOK) or bilayer-like films with silicon oxy nitride (as a 2^(nd)layer) or other etch stop material for the upper via level.

An insulator layer 14 is formed on the layer 12. In embodiments, theinsulator layer 14 can be an ultra low dielectric material, e.g., k<2.2:although other insulator materials are contemplated by the presentinvention. In embodiments, the insulator layer 14 can be fluorinatedsilica glass, carbon-doped silicon dioxide, porous silicon dioxide orspin-on organic polymeric dielectrics as examples. The insulator layer14 can be deposited using conventional chemical vapor deposition (CVD)or plasma enhanced CVD (PECVD) processes, as examples.

Still referring to FIG. 1, a plurality of metal lines 16 are formed withspacing 18 therebetween. In embodiments, the metal lines 16 have equalline spacing 18 therebetween; although other spacing is contemplated bythe present invention based on technology nodes and other designcriteria. For example, the width of the metal lines 16 can be largerthan the spacing 18. In any scenario, in embodiments, the metal lines 16can be copper material forming wires or vias; although other metal ormetal alloy material is also contemplated by the present invention.

The metal lines 16 can be formed using conventional damascene processes.For example, in embodiments, the insulator layer 14 can be patternedusing conventional lithography and etching processes, e.g., reactive ionetching (RIE), to form openings. Conductive material, e.g., copper, canbe deposited within the openings, following by a chemical mechanicalpolishing to planarize the metal layer and remove any residual metalmaterial from a surface of the insulator material. The conductivematerial can be deposited using conventional CVD or PECVD processes,amongst other deposition processes.

The insulator material between the metal lines 16 can be removed usingconventional dry etching processes, e.g., RIE, to form the spacing 18between the metal lines 16. In embodiments, insulator material 14 a canremain between selected metal lines 16 in order to provide rigidity andmaintain the integrity of the structure. For example, the insulatormaterial 14 a can be aligned with an upper via or located at a positionthat is devoid of any critical features.

FIG. 2 shows formation of air gaps 22 between metal lines 16 andrespective fabrication processes in accordance with aspects of theinvention. More specifically, as shown in FIG. 2, a capping material 20is formed over the metal lines 16 and within the spacing 18. The cappinglayer 20 can be deposited using a conventional CVD, PECVD or otherdeposition process. During the deposition process, the capping layer 20will line the sidewalls of the metal lines 16, following by pinching offthe spacing 18 forming the air gaps 22. That is, the capping layer 20will be pinched off prior to completely filling the spacing 18, therebyresulting in capping material on the sidewalls of the metal lines and anair gap 22 within the spacing 18. The deposition process will continueuntil the capping material 20 forms a layer over the metal lines 16 andany insulator material 14 a. The capping material 20 can optionally beplanarized using a conventional CMP process. In embodiments, the cappingmaterial 20 can be nitride of other NBLOK material or other diffusionbarrier material.

In FIG. 3, an insulator material 24 is deposited on the capping material20. In embodiments, the insulator material 24 can be an ultra lowdielectric material, e.g., k<2.2; although other insulator aterials arealso contemplated by the present invention as described herein. Theinsulator material 24 can be patterned to form trenches 26 and 28 usingconventional lithography and etching processes as described herein. Inembodiments, the trenches 26 and 28 have offset depths, e.g., trench 26is deeper than the trench 28. In this way, the trench 26 will forth partof a deep plate capacitor structure; whereas, the trench 28 will form aconventional interconnection structure, as an example.

In embodiments, the trenches 26 and 28 are formed using conventionallithography and etching (RIE) processes. For example, the trench 28 canbe formed by first punching through a TiN hardmask to etch an initialdepth in the insulator material. Thereafter, both trenches 26 and 28undergo a RIE process to form the respective depths of the trenches 26and 28. Iii alternative embodiments, the deeper trench 26 can be formedby an engineered reverse RIE lag process which results in a deepertrench due its larger cross sectional area (compared to the trench 28).After trench formation,any remaining masking material can be removedusing an oxygen ashing process or other conventional strippingtechnique.

FIG. 4 shows a process to open the air gaps 22 in accordance withaspects of the present invention. By way of illustration, an etchingprocess can be used to provide an opening 30 to the air gaps 22, bymaking the trench aligned with the air gaps 22 deeper as shown byreference numeral 26′. The etching process will also remove insulatormaterial 24 from the bottom of the trench 28; however, this etchingprocess will not open the underlying air gap(s) since trench 28 was notas deep as original trench 26.

In FIG. 5, a conductive material 32 is deposited within the trenches26′, 28, as well as within the opened air gaps 22 (and overlying theadjacent pair of bottom metal lines). In embodiments, the conductivematerial 32 can be copper or other metal or metal alloy deposited usingany conventional deposition process such as CVD, PECVD or an atomiclayer deposition (ALD). The deposition process can be followed by areflow of the metal material 32 to ensure adequate coverage within theair gaps 22.

The conductive material 32 within the air gaps 22 can be used as groundsfor a capacitor plate which comprises the metal lines 16, cappingmaterial 20 on the sidewalls of the metal lines 16, and the metalmaterial 32. The capacitance of the structure can be set by adjustingthe thickness and/or dielectric of the capping material 20 on thesidewalls of the metal lines 16.

The method(s) as described above is used in the fabrication ofintegrated circuit chips. The resulting integrated circuit chips can bedistributed by the fabricator in raw wafer form (that is, as a singlewafer that has multiple unpackaged chips), as a bare die, or in apackaged form. In the latter case the chip is mounted in a single chippackage (such as a plastic carrier, with leads that are affixed to amotherboard or other higher level carrier) or in a multichip package(such as a ceramic carrier that has either or both surfaceinterconnections or buried interconnections). In any case the chip isthen integrated with other chips, discrete circuit elements, and/orother signal processing devices as part of either (a) an intermediateproduct, such as a motherboard, or (b) an end product. The end productcan be any product that includes integrated circuit chips, ranging fromtoys and other low-end applications to advanced computer products havinga display, a keyboard or other input device, and a central processor.

The descriptions of the various embodiments of the present inventionhave been presented for purposes of illustration, but are not intendedto be exhaustive or limited to the embodiments disclosed. Manymodifications and variations will be apparent to those of ordinary skillin the art without departing from the scope and spirit of the describedembodiments. The terminology used herein was chosen to best explain theprinciples of the embodiments, the practical application or technicalimprovement over technologies found in the marketplace, or to enableothers of ordinary skill in the art to understand the embodimentsdisclosed herein.

What is claimed:
 1. A back end of line capacitor comprising: a bottomplate comprising a plurality of metal lines separated by spacing; adielectric layer lining the metal lines within the spacing; and a topplate above the metal lines and within the spacing over the dielectricmaterial.
 2. The back end of line capacitor of claim 1, wherein the topplate is provided within a trench of insulator material and over thespacing between the metal lines of the bottom plate.
 3. The back end ofline capacitor of claim 1, wherein air gaps are provided between theplurality of metal lines of the bottom plate.
 4. The back end of linecapacitor of claim 1, wherein the airgaps are pinched off material ofthe dielectric layer.
 5. The back end of line capacitor of claim 4,wherein the dielectric layer is pinched off prior to completely fillingthe spacing separating the plurality of metal lines of the bottom plate.6. The back end of line capacitor of claim 1, wherein the dielectriclayer comprises a planarized surface.
 7. The back end of line capacitorof claim 1, wherein the dielectric layer is nitride material.
 8. Theback end of line capacitor of claim 1, further comprising insulatormaterial deposited on the dielectric layer.
 9. The back end of linecapacitor of claim 8, wherein the insulator material is an ultra lowdielectric material.
 10. The back end of line capacitor of claim 8,wherein the insulator material has trenches and the top plate is in thetrenches.
 11. The back end of line capacitor of claim 10, wherein thetrenches have offset depths.
 12. The back end of line capacitor of claim11, wherein the top plate is provided over the spacing between the metallines of the bottom plate.
 13. The back end of line capacitor of claim12, wherein the top plate is provided within the spacing between theplurality of metal lines of the bottom plate, separated from theplurality of metal lines of the bottom plate by the dielectric layer.14. The back end of line capacitor of claim 13, wherein the top plateprovided within the spacing is formed in an airgap that has an openedupper portion.